Bituminous primer made with blown bitumen and hi-tech solvents. POLYPRIMER is used as a primer for concrete surfaces, to stop dusting and saturate their porosity, allowing traditional or…
Bituminous primer made with blown bitumen and hi-tech solvents. POLYPRIMER is…
TECHNICAL DATA: Consistency: paste. Application temperature range: from +5°C to +35°C. Waiting time between first and second coat: 8-12 hours. Set to foot traffic: 12 hours at +23°C. Colour: highly…
TECHNICAL DATA: Consistency: paste. Application temperature range: from +5°C to…
76533005002 - POLYFOND KIT DRAIN 76533025001 - POLYFOND KIT FIXING BOX 200PC 76533020001 - POLYFOND KIT PROFILE H POLYFOND KIT DRAIN is a protection and drainage system made from high-density…
76105230001 - Evolight S 3 mm 76105245002 - Evolight S 4.5 mm Cold flexibility: -10°C EVOLIGHT S is a plastomeric waterproofing membrane with outstanding performance. It is made using the latest…
76105230001 - Evolight S 3 mm 76105245002 - Evolight S 4.5 mm Cold flexibility:…
TECHNICAL DATA: Movement in service (%): 25 (with PRIMER M or PRIMER A). Modulus of elasticity at 100% elongation: 0.8 N/mm². Shore A hardness (DIN 53505): 36. Workability time: 90 minutes. Colour:…
TECHNICAL DATA: Movement in service (%): 25 (with PRIMER M or PRIMER A).…
TECHNICAL DATA: Mixing ratio: A/B/C = 1.6/1.4/18 plus 0.25 parts by weight of MAPECOLOR PASTE. Colour of mix: depending on the colour of MAPECOLOR PASTE used. Pot life of mix at +20°C: 20 minutes.…
TECHNICAL DATA: Mixing ratio: A/B/C = 1.6/1.4/18 plus 0.25 parts by weight of…
TECHNICAL DATA: Type of fibre: A.R. type glass fibre. Weight: 225 g/m ² . Mesh size: 25 x 25 mm. Tensile strength (kN/m): 45. Elongation at failure: < 3%. Packaging: 45.70 m x 90 cm rolls.
TECHNICAL DATA: Type of fibre: A.R. type glass fibre. Weight: 225 g/m ² . Mesh…
DESCRIPTION: Synthetic resin-based primer in solvent solution to improve the adhesion of liquid elastic membranes (from the Aquaflex Roof line) onto existing bituminous membranes
DESCRIPTION: Synthetic resin-based primer in solvent solution to improve the…
DESCRIPTION: Two-component thixotropic epoxy adhesive with long workability time for structural bonds. TECHNICAL DATA: Mixing ratio: comp. A : comp. B = 3 : 1. Pot life of mix: 50 minutes (at +23°C).…
DESCRIPTION: Two-component thixotropic epoxy adhesive with long workability…
Adhesive zinc plates applied directly on the surface of structures for galvanic cathodic protection against the corrosion of reinforcement rods in concrete. Mapeshield E comprises a 99.9% pure zinc…
Adhesive zinc plates applied directly on the surface of structures for galvanic…
TECHNICAL DATA: Consistency: thixotropic. Mixing ratio: comp. A: comp. B = 2.2 : 1. Pot life of mix: approximately 1 hour (at +20°C). Application temperature range: from +5°C to +40°C. Minimum…
TECHNICAL DATA: Mixing ratio: A/B/C = 2.6/2.7/20.5 plus 5 kg of MAPECOLOR CPU. Colour of mix: grey, beige, ochre, red and green. Consistency of mix: thick. Pot life of mix at +20°C: 15 minutes. Dust…
TECHNICAL DATA: Mixing ratio: A/B/C = 2.6/2.7/20.5 plus 5 kg of MAPECOLOR CPU.…
TPE tape for flexible sealing and waterproofing expansion joints and cracks subject to movements up to 5 or 10 mm, using Mapeband TPE 170 or Mapeband TPE 325 respectively. It is particularly…
TPE tape for flexible sealing and waterproofing expansion joints and cracks…
TECHNICAL DATA: Maximum dimension of aggregate: 1.5 mm. Mixing ratio: 1 25 kg comp. A with 1 drums of comp. B. Pot life of mix: approximately 1 hour (at +20°C). Thickness applied: from 3 to 10 mm per…
TECHNICAL DATA: Maximum dimension of aggregate: 1.5 mm. Mixing ratio: 1 25 kg…
TECHNICAL DATA: Maximum dimension of aggregate: 1 mm. Mixing ratio: 4 parts of PLANITOP HDM MAXI comp. A with 1 part of PLANITOP HDM MAXI comp. B. Pot life of mix: approximately 1 hour (at +20°C).…
TECHNICAL DATA: Maximum dimension of aggregate: 1 mm. Mixing ratio: 4 parts of…