MAPESTONE PFS CALCIX

Pre-blended, cement-free, lime-based mortar with high recycled material content for installation beds for grouting pavements, piazzas and roads in stone not used by heavy traffic, including those of historical interest.

MAPESTONE PFS CALCIX

Pre-blended, cement-free, lime-based mortar with high recycled material content for installation beds for grouting pavements, piazzas and roads in stone not used by heavy traffic, including those of historical interest.

SUITABLE FOR AREAS HIGHLY SATURATED WITH WATER

MADE FROM NATURAL HYDRAULIC LIME (NHL), ZERO CEMENT CONTENT

IDEAL FOR PEDESTRIAN AND LIGHT VEHICLE TRAFFIC

LOW ENVIRONMENTAL IMPACT THANKS TO ITS HIGH RECYCLED MATERIAL CONTENT

MAPESTONE CALCIX is a cement-free system specific for refurbishing and restoring stone paving, including of historical interest.

MAPESTONE PFS CALCIX is recommended for grouting decorative stone paving used by light vehicle traffic.

MAPESTONE PFS CALCIX can be used to create durable, class P4, P5, P6 and P7 decorative stone paving in compliance with UNI 11714-1:2018, including in areas highly saturated with water.

REQUEST A CONSULTATION

MAPESTONE PFS CALCIX

Pre-blended cement-free mortar made from lime with good mechanical properties and resistance to freezing weather specific for grouting class P4, P5, P6 and P7 decorative stone paving, including of historical interest, compliant with UNI 11714-1:2018 standard for use by pedestrians and light vehicles

ADVANTAGES:

Made from natural hydraulic lime (NHL), zero cement content
Ideal for pedestrian and light vehicle traffic
Low environmental impact thanks to its high recycled material content
Suitable for areas highly saturated with water

Product consistency: powder
Colours: light (Mapestone PFS Calcix) and
dark grey (Mapestone PFS Tenebris)
Maximum particle size: 3 mm
Approximate width of joints: 5-30 mm
Mixing ratio: 4-4.25 l of water per 25 kg bag
Mixing water (%): 16-17
Density when wet (kg/m³): 2100
Dynamic modulus of elasticity (air cured) (MPa): 20000
Flexural strength after 28 days of air curing (MPa)
(UNI 13892-2): 3.8
Flexural strength of hardened mortar (MPa) (EN 1015): 3.1
Compressive strength after 28 days of air curing (MPa)
(UNI 13892-2): 17.1
Compressive strength of hardened mortar (MPa) (EN 1015): 24.3
CAP-ON abrasion test (mm³) (EN 12808-2): 164